A Vinyl Chloride-Vinyl Acetates- Maleic Acid Terpolymer
Application:
Vinyl Resin JA, JB, JC are mainly used as adhesives for gun nail, PCB adhesive and PVC decoration sheet adhesives.
Carboxyl Type
Spec/
Item |
UMCH |
JA |
JB |
JC |
MC39 |
Measuring Method and Code |
||
52 |
55 |
58 |
||||||
Appearance |
White Powder |
Visual |
||||||
Adhesion Number ml/g K Value |
50-52 |
54-56 |
57-59 |
60-62 |
55-57 |
55-57 |
37-39(36-37) |
GB/T 34011999 Calculated Based on Adhesion Number |
Vinyl Acetates Content by mass % |
13-15 |
13-15 |
13-15 |
11-13 |
11-13 |
13-15 |
24-26 |
Q/320205AHAD06 2006 |
Maleic Acid Content% |
1.8-2.1 |
1.8-2.1 |
1.8-2.1 |
1.6-2.0 |
1.6-2.0 |
3.6-4.0 |
0.9-1.1 |
Q/320205AHAD01 2006 |
Volatile Contents including moisture |
1.0 |
GB/T 2914-1999 |
||||||
Pile Density (g/ml) |
0.60 |
GB/T 3402 Appendix A |
||||||
Solubility 25%MEK: TOLUENE 1 1 |
Colorless, Transparent, No non-soluble Particles |
Visual |
Recommendation for Resin Dissolving Procedure:
Add weak solvent such as ethyl acetate or toluene into the blending tank first with agitation.
Slowly put terpolymer resin such as UMCH or UMOH into the above solvents with agitation.
Put strong solvents last, such as MEK or MIPK
If possible, heating and keeping temperature at 60-70 degree C, which will help the dissolving process, otherwise, takes longer time.
Resin concentration may vary with client’s formulation
Features:
This terpolymer contains carboxyl group, therefore, it features good adhesions to aluminum foil, also because it contains PVC so, also has good resistance to alkali, base, brine, salty mist, also has good resistance to oil ester and alcohols.
Packing and Storage:
25 Kg /Bag; Craft Paper Bag or PP Knitted Bag lined with plastic film.
Stored in dry place at room temperature, Safety Issue refer MSDS and SGS Repor